Kinematic Viscosity, at 100°C, cSt min.
|
|
2.0
|
|
High Temp. Stability, °C change, max.
|
|
1°C(2°F)
|
|
Chemical Stability, °C change, max.
|
|
1°C(2°F)
|
|
Inversion Time at -40°C
|
|
6
|
|
Inversion Time at -50°C
|
|
7
|
|
Stroking Properties
|
|
Pass
|
|
Equilibrium Reflex Boiling Point, °C (°F) min.
|
|
256 (494)
|
|
Wet Equilibrium Reflex Boiling Point, °C (°F) min.
|
|
145 (292)
|
|
Corrosion weight change, mg/cm2, max.
Tinned Iron
|
|
0.00
|
|
Corrosion weight change, mg/cm2, max.
Steel
|
|
0.01
|
|
Corrosion weight change, mg/cm2, max.
Aluminum
|
|
0.01
|
|
Corrosion weight change, mg/cm2, max.
Cast Iron
|
|
0.01
|
|
Corrosion weight change, mg/cm2, max.
Brass
|
|
0.02
|
|
Corrosion weight change, mg/cm2, max.
Copper
|
|
0.02
|
|
Evaporation at 100 °C:
Loss in weight, % max.
|
|
32.8
|
|
Evaporation at 100 °C:
Pour point of residue, °C max.
|
|
<-5
|
|
Water tolerance:
Inversion time at -40°C, sec., max.
|
|
2
|
|
Water Tolerance:
Sedimentation at 60°C, vol. %, max.
|
|
0.0
|
|
Compatibility:
Sedimentation at 60°C, vol. % max.
|
|
<0.00
|
|
Resistance to oxidation - Wt. change, mg/cm2, amx.
Aluminum
|
|
0.00
|
|
Resistance to oxidation - Wt. change, mg/cm2, amx.
Cast Iron
|
|
0.02
|
|
Effects on rubber cups at 70°C:
Base diameter increase, mm
|
|
0.15
|
|
Effects on rubber cups at 70°C:
Hardness decrease, IRHD, max.
|
|
2
|
|
Effects on rubber cups at 120°C:
Base diameter increase, mm
|
|
0.22
|
|
Effects on rubber cups at 120°C:
Hardness decrease, IRHD, max.
|
|
3
|
|
Kinematic Viscosity, at -40°C, cSt
|
|
936
|
| |
#Eaches |
Weight |
Length |
Height |
Width |
| Each |
|
2.413 |
3.375 |
8.938 |
3.375 |
| Case |
12 |
28.953 |
14.500 |
9.375 |
11.000 |
| Pallet |
660 |
1592.422 |
48.000 |
51.875 |
40.000 |